The influence of prior creep damage on the fracture localisation in X20 CrMoV12-1 cross-weld creep tests
Many of Eskom's coal fired power plants have an average age of 170 000 hours and a few operating close to 300 000 hours. Main steam temperatures experienced in a power plant vary between 535-555°C. These operating conditions place main steam pipe components to operate within the creep regime. It is...
Saved in:
| Main Author: | |
|---|---|
| Other Authors: | |
| Format: | Thesis |
| Language: | English |
| Published: |
Centre for Materials Engineering
2018
|
| Subjects: | |
| Tags: |
No Tags, Be the first to tag this record!
|
Similar Items: The influence of prior creep damage on the fracture localisation in X20 CrMoV12-1 cross-weld creep tests
- Continuum Damage Mechanics (CDM) modelling of dislocation creep in 9-12% Cr creep resistant steels
- Microstructural and property assessment of creep aged 12cr steel after welding
- The modelling of damage due to diffusional creep in high chromium steels
- Susceptibility of creep aged material to stress relief cracking during repair welding
- Susceptibility of service exposed creep resistant materials to reheat cracking during repair welding
- Creep predictions for turbomachinery components