Studying water-wedging as a cause for short term overheating in the boiler of a coal-fired power plant
A common failure occurrence on fossil fuel power plant boiler systems is referred to as short term overheating (STO). This phenomenon occurs when the tube is heated to higher than its design temperature in a short period of time, causing a ductile failure of the tube material. The superheaters are p...
Saved in:
| Main Author: | |
|---|---|
| Other Authors: | |
| Format: | Thesis |
| Language: | English |
| Published: |
Department of Mechanical Engineering
2019
|
| Subjects: | |
| Tags: |
No Tags, Be the first to tag this record!
|
| _version_ | 1867613237243019264 |
|---|---|
| access_status_str | Open Access |
| author | Basson, Nicol |
| author2 | Fuls, Wim |
| author_browse | Basson, Nicol Fuls, Wim |
| author_facet | Fuls, Wim Basson, Nicol |
| author_sort | Basson, Nicol |
| collection | Thesis |
| description | A common failure occurrence on fossil fuel power plant boiler systems is referred to as short term overheating (STO). This phenomenon occurs when the tube is heated to higher than its design temperature in a short period of time, causing a ductile failure of the tube material. The superheaters are particularly susceptible to STO. Such a failure can be caused by various conditions, where most of these are condition-based, i.e. based on the physical condition of the pipes or boiler. However, there are some cases which are process-related, i.e. based on the thermo-physical process occurring inside the pipe. Very often a water blockage or water wedge is recorded to be the root cause of the short term overheating in superheaters when no condition-based indicators can be found. It then is claimed to be the result of over-attemperation spray by the operator. This type of failure tends to happen at the outlet of vertical (pendant-type) superheaters. This study aims to find thermo-physical conditions where such a conclusion is valid by studying the transient behaviour of a representative superheater segment under postulated conditions. The specific geometry chosen is one for which short term overheating due to water wedging has been recorded in the past. A transient flow model was constructed and verified by comparing its results with plant data, as well as some results from a numerical model developed from fundamental principles. Once the simulation modelling methodology was confirmed, the model was modified to resemble the geometry of the final superheater outlet leg to facilitate direct comparison with a pendant boiler component as found on a power plant. A number of scenarios were executed in transient state on the model at different boiler loads. The temperature evolution of the pipe wall was tracked over time, and together with calculated equivalent stresses, was compared to the yield strength of the material. A temperature vs yield strength curve was obtained from material testing using new and aged tube material. The results showed that short term overheating at the superheater outlet tubes due to water blockages alone is unlikely to occur, even at low loads and substantial over firing. The stresses exerted over the tube wall and throughout the tube length is not enough to overcome the yield stress of the superheater tube material, even for aged material. Thus, the claim of overattemperation as the root cause of a short term overheating failure is improbable, and other explanations for the failure must be observed. Even though it is possible for water-wedging to occur, the phenomenon alone is unlikely to be the root cause for the occurrence of short term overheating. |
| format | Thesis |
| id | oai:open.uct.ac.za:11427/29585 |
| institution | University of Cape Town (South Africa) |
| language | eng |
| last_indexed | 2026-06-10T12:32:57.328Z |
| license_str | Not specified — see source repository |
| provenance_str_mv | Harvested via OAI-PMH from UCTD — University of Cape Town Open Access Repository |
| publishDate | 2019 |
| publishDateRange | 2019 |
| publishDateSort | 2019 |
| publisher | Department of Mechanical Engineering |
| publisherStr | Department of Mechanical Engineering |
| record_format | dspace |
| source_str | UCTD — University of Cape Town Open Access Repository |
| spelling | oai:open.uct.ac.za:11427/29585 Studying water-wedging as a cause for short term overheating in the boiler of a coal-fired power plant Basson, Nicol Fuls, Wim Mechanical Engineering A common failure occurrence on fossil fuel power plant boiler systems is referred to as short term overheating (STO). This phenomenon occurs when the tube is heated to higher than its design temperature in a short period of time, causing a ductile failure of the tube material. The superheaters are particularly susceptible to STO. Such a failure can be caused by various conditions, where most of these are condition-based, i.e. based on the physical condition of the pipes or boiler. However, there are some cases which are process-related, i.e. based on the thermo-physical process occurring inside the pipe. Very often a water blockage or water wedge is recorded to be the root cause of the short term overheating in superheaters when no condition-based indicators can be found. It then is claimed to be the result of over-attemperation spray by the operator. This type of failure tends to happen at the outlet of vertical (pendant-type) superheaters. This study aims to find thermo-physical conditions where such a conclusion is valid by studying the transient behaviour of a representative superheater segment under postulated conditions. The specific geometry chosen is one for which short term overheating due to water wedging has been recorded in the past. A transient flow model was constructed and verified by comparing its results with plant data, as well as some results from a numerical model developed from fundamental principles. Once the simulation modelling methodology was confirmed, the model was modified to resemble the geometry of the final superheater outlet leg to facilitate direct comparison with a pendant boiler component as found on a power plant. A number of scenarios were executed in transient state on the model at different boiler loads. The temperature evolution of the pipe wall was tracked over time, and together with calculated equivalent stresses, was compared to the yield strength of the material. A temperature vs yield strength curve was obtained from material testing using new and aged tube material. The results showed that short term overheating at the superheater outlet tubes due to water blockages alone is unlikely to occur, even at low loads and substantial over firing. The stresses exerted over the tube wall and throughout the tube length is not enough to overcome the yield stress of the superheater tube material, even for aged material. Thus, the claim of overattemperation as the root cause of a short term overheating failure is improbable, and other explanations for the failure must be observed. Even though it is possible for water-wedging to occur, the phenomenon alone is unlikely to be the root cause for the occurrence of short term overheating. 2019-02-18T10:08:31Z 2019-02-18T10:08:31Z 2018 2019-02-18T10:07:10Z Master Thesis Masters MSc (Eng) http://hdl.handle.net/11427/29585 eng application/pdf Department of Mechanical Engineering Faculty of Engineering and the Built Environment University of Cape Town |
| spellingShingle | Mechanical Engineering Basson, Nicol Studying water-wedging as a cause for short term overheating in the boiler of a coal-fired power plant |
| thesis_degree_str | Master's |
| title | Studying water-wedging as a cause for short term overheating in the boiler of a coal-fired power plant |
| title_full | Studying water-wedging as a cause for short term overheating in the boiler of a coal-fired power plant |
| title_fullStr | Studying water-wedging as a cause for short term overheating in the boiler of a coal-fired power plant |
| title_full_unstemmed | Studying water-wedging as a cause for short term overheating in the boiler of a coal-fired power plant |
| title_short | Studying water-wedging as a cause for short term overheating in the boiler of a coal-fired power plant |
| title_sort | studying water wedging as a cause for short term overheating in the boiler of a coal fired power plant |
| topic | Mechanical Engineering |
| url | http://hdl.handle.net/11427/29585 |
| work_keys_str_mv | AT bassonnicol studyingwaterwedgingasacauseforshorttermoverheatingintheboilerofacoalfiredpowerplant |